ASTM A213 Grade T11 ezali tube ya chrome ferritique-molybdène (Cr-Mo) sans soudure oyo esalelamaka na ba environnements ya vapeur ya moto mpe ya combustion-gaz. Grade yango esalemi mpo na ba composants oyo ezali na pression-na ba chaudières ya puissance, ba HRSG, ba chauffe-eau pétrochimiques mpe ba échangeurs ya chaleur ya température ya likolo esika oyo acier carbone ekoki te kosimba résistance ya oxydation to makasi ya creep.
Octal Pipe epesaka T11 na condition normalisé-mpe-tempered, na contrôle dimensionnel, test complet na ASTM A213/A1016 mpe na ba certificats ya moulin, mpo ekoki kokende mbala moko na fabrication ya chaudière mpe ya procédé.

astm a213 t11 tubing bundles for boiler and superheater service - octal pipe

Composition chimique oyo esalemi

Eloko	Makambo eza na kati (%)	Mosala
C	0.05 – 0.15	Epesaka makasi mpe résistance ya creep, etikalaka soudable
Mn	0.30 – 0.60	Ductilité, mosala ya molunge
Si	0.50 – 1.00	Esungaka résistance ya oxydation
P	Na nse to ekokani na 0,025	Ezali kopekisa kolɛmba nzoto
S	Na nse to ekokani na 0,025	Contrôlé mpo na duresse
Cr	1.00 – 1.50	Résistance ya échelle na vapeur / gaz ya combustion
Mo	0.44 – 0.65	Creep mpe makasi ya rupture

Equilibre oyo ya chrome–molybdène ezali na se koleka T22 to ba grades misusu ya likolo-Cr, yango wana T11 egumbamaka mpe e soudure na pete, kasi ebikaka kaka na service ya 500–600 degrés.

Bizaleli ya masini

Lopango	Esengeli oyo esengeli	Mokano
Bokasi ya kokangama	Monene koleka to ekokani na 415 MPa (60 ksi) .	Capacité ya chargement mobimba
Bokasi ya mbuma (0,2%) .	Monene koleka to ekokani na 205 MPa (30 ksi) .	Epekisaka déformation permanente
Elongation ya nzoto	Monene koleka to ekokani na 30% .	Esengeli mpo na kogumbama, kobalusa, kosouda
Bokasi ya makasi	Na nse to ekokani na 163 HBW	Ebatelaka duresse mpo na cyclisme thermique

Ba valeurs oyo ekokani na condition ya livraison normalisée-et-tempered oyo ba projets ya puissance na raffinerie elakisaka mingi.

Kosala mpe kosala yango na molunge

Pona service ya tube ya chaudière route eza na tina mingi lokola chimie. Octal Pipe esalela nzela ya kozanga boyokani na nse ya ASTM A213/A1016:

billet ya alliage ezali moto-percé to extrudé mpo na kosala creux ya son
tube ezali moto-roulé to malili-bendami na OD oyo epesameli mitindo, efelo mpe likolo ya kosilisa (ya ntina mpo na ba tubes ya échangeur ya molunge-)
tube e normaliser na soki 940–980 degrés mpo na ko refiner matrice ferritique, kolongola bande mpe ko égaliser ba propriétés mécaniques na longueur
tube e temper na soki 675–755 degrés mpo na kozongisa ductilité mpe kokanga dispersion ya malamu ya ba carbures na esika na yango

Cycle oyo ya N+T nde epesaka T11 microstructure na yango ya stable : chrome ekoki kotonga film ya oxyde serré, molybdène ekoki kosala mosala na yango na renforcement ya creep, mpe tube ekomaka trop difficile te mpo na soudure. Sima ya traitement ya chaleur, ba tubes ezo sedresser, ezo tester hydrostatique, pe ezo examiner na méthode ya NDE oyo e commander (eddy-courant to ultrasonique) avant ya ko marquer pe ko emballage. Etape nionso e enregistrer donc tube ezala traçable sima na chaleur.

Range ya dimension

Paramètre	Range / makambo ya mikemike
Diamètre ya libanda	12,7 – 127 mm (0,5 – 5 na bonene)
Épaisseur ya mur	1,2 – 12 mm
Bolai	Kino na mɛtrɛ 12; SRL / DRL / kokata-na-bolai
Suka kosilisa	Plain, biseauté, to ebongisami mpo na U-bending / finning
Tolerance ya OD	na momeseno ± 1% (na ASTM A1016) .
Tolerance ya mur	na momeseno ± 10% .
Kozala semba	mingi mingi Moke to ekokani na 0,8 mm/m

Yango etali ba tubes ya panneau ya chaudière oyo emonanaka mingi, ba bobines ya superchauffe-eau/réchauffe-eau, mpe ba bobines ya chauffe-eau ya raffinerie.

Bosali ya mosala

Na fonctionnement T11 esali oxyde uniforme riche en chrome-, yango wana perte ya métal ya tube na build ya échelle-up ezali malembe koleka na acier carbone. Molybdène elɛmbisaka kopumbwa mpe kobukana, oyo ezali na ntina mingi mpo na ba tubes oyo efandaka na nse ya molunge mpe na pression na boumeli ya bankóto ya bangonga. Lokola structure ezali ferrite tempéré, tube e tolérer ba cycles ya début–arrêt na ba HRSGs na ba usines ya cogénération sans ko perdre droit noki mingi. Ba soudures ebatelaka intégrité sima ya PWHT tango ba métaux ya remplissage ya alliage faible-qualifié esalelami.

Ba applications

mur d’eau ya chaudière, superchauffe-eau, réchauffe-eau mpe ba tubes économisateur na ba centrales électriques thermiques
HRSG / ba générateurs ya vapeur ya cycle combiné-
ba chauffe-eau ya procédé pétrochimie mpe ya raffinerie
ba échangeurs ya chaleur ya coquille ya température ya likolo-mpe-tube
ba lignes ya utilité ya moto mpe ya procédé na kati ya ba unité ya puissance na chimique

Botali mpe mikanda

Bomeki esalemi engebene na ASTM A213 mpe masengi ya générale ya A1016. Yango esangisi examen hydrostatique to eddy-current pona ba tests ya sonance ya mur, ya traction na duresse par lote ya traitement ya chaleur-, aplat/flaring pona ko prouver ductilité, plus inspection visuelle et dimensionnelle. Pona ba projets oyo ezali na QA/QC ya likolo, Octal Pipe ekoki kobakisa ba vérifications ultrasoniques to radiographiques. Ba tubes nionso epesami na EN 10204 3.1 to 3.2 MTC po nkolo akoki ko déposer ba résultats chimiques, mécaniques na NDE na numéro ya chaleur.

Pourquoi source ASTM A213 T11 na Octal Pipe

vrai tube sans soudure Cr-Mo na état normalisé-et-temperé, kaka tube ya carbone générique-acier te
ba dimensions, ba tests pe marquage oyo ezo aligné na ba spécifications ya puissance, chaudière, HRSG pe raffinerie
export-ba faisceaux prêts na protection ya suka pona envoi ya ntaka molai-
soutien ya ingénierie mpo na ko correspondre T11 na ba grades ya Cr-Mo oyo etali yango (T22, A335 P11/P22) tango unité moko esalelaka ba alliages ebele
structure ya page produit ekomami-ya liboso mpe techniquement spécifique, mpo na kosunga site na yo ya sika ezua indexé lokola page ya fournisseur, kasi contenus ya modèle te

Mituna oyo batunaka mingi